| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | 280 |
| Density | g mL-1 | 1.35 |
| Coefficient of Thermal Expansion | cm / (cm °C) x 10-5 | 5.2 - 5.3 |
| Heat Deflection Temperature, 0.5 MPa | °C | |
| Heat Deflection Temperature, 1.8 MPa | °C | 115 - 120 |
| Thermal Conductivity | W / mK | 0.29 - 0.32 |
| Rockwell Hardness, M Scale | n/a | M90 - M100 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | |
| Tensile Strength, Break at 23 C | MPa | 33 - 90 |
| Elongation, Yield | % | |
| Elongation, Break | % | 1.0 - 8.0 |
| Tensile Modulus at 23 C | MPa | 3800 - 4200 |
| Flexural Strength, Break | MPa | 125 - 135 |
| Flexural Modulus | MPa | 3750 - 3900 |
| Compressive Strength, 1% - 2% | MPa | |
| Charpy Impact Strength | kJ/m2 | 8.0 - 45 |
| Izod Unnotched | kJ/m2 | 2.0 - 3.5 |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm x 1014 | 109 | |
| Dielectric Strength | V/mm x 104 | 1.7 - 1.8 | |
| Dielectric Constant @ 1 MHz | n/a | 4.0 - 4.5 | |
| Dissipation Factor @ 1 MHz | n/a, x 10-4 | 11 - 84 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 305 - 320 | |
| Mold Shrinkage | % | 0.001 - 0.003 | |
| Continuous Service Temperature | °C | ||
| Water Absorption, 24 hr. Immersion | % | 0.02 |